谁能帮我翻译成英语吗? 谢谢!!翻译的好的,加分!!一定要准!! 谢谢!!

1.测试结束后,在常温(25℃±5℃)下放置1小时后进行测试.要满足目录3(6Page)的电子2.要满足目录3(6Page)的电子特性.无外观损坏及变性不良3.Cycle... 1.测试结束后,在常温(25℃±5℃)下放置1小时后 进行测试.
要满足目录3(6Page)的电子
2. 要满足目录3(6Page)的电子特性.
无外观损坏及变性不良
3. Cycle: 30 cycles (各1个小时 总60小时(低温 30hr.高温 30hr.))
4. 高度 152cm. 落下19次(铁板)
5. 实验结束后 用蒸馏水清洗后 在2个小时之内 进行外观检查
表面无腐蚀,脱离.
6. Tape 黏贴测试 连续进行2次
Tape 黏贴测试后 Cutting的部分 Plating面 不能有脱落
7. 2mm 5行以上 tape 黏贴测试 2回
8.把尾部固定在Torque Gage .
9.把尾部固定
10.High=162cm 19次 落下 ,地板(铁板)
11.把中间 push/full gauge
12.每个样品,测试10个产品
请知道的大侠帮帮忙!!! 谢谢了!!
展开
最爱错过
2012-08-15
知道答主
回答量:19
采纳率:0%
帮助的人:10.5万
展开全部
1. Test ended, in room temperature (25 ℃ ± 5 ℃) for 1 hour after testing.
To meet the directory 3 (6 page) electronic
2. To meet the directory 3 (6 page) electronic characteristics.
No appearance damage and degeneration bad
3. Cycle: 30 cycles (each 1 hours total 60 hours (low temperature 30 hr. High temperature 30 hr.)
4. Height 152 cm. Fall 19 (iron)
5. After the experiment with distilled water after cleaning in two hours for appearance inspection
Surface no corrosion, from.
6. Tape affixes test continuous twice
Tape affixes testing Cutting part Plating surface can't have fall off
7. 2 mm five line above tape affixes test 2 back
8. The tail fixed in Torque Gage.
9. The tail fixed
High = 162 cm 19 fall, the floor (iron)
11. The middle push/full gauge
12. Each sample, test 10 products
已赞过 已踩过<
你对这个回答的评价是?
评论 收起
kxzjp999
2012-08-07 · TA获得超过228个赞
知道答主
回答量:207
采纳率:100%
帮助的人:19.7万
展开全部
1 after the end of the test, for 1 hour at room temperature (25 ° C ± 5 ° C) tested
to meet the electronic catalog 3 (6Page)
2 to meet the electronic properties of the catalog 3 (6Page)
cosmetic damage and degeneration bad
3. Cycle: 30 cycles (each 1 hour 60 hours (30hr low-temperature high-temperature 30hr))
. height of 152cm. down 19 times (iron)
. end of the experiment with distilled water after 2 hours within the visual inspection of
surface corrosion, out of
6. Tape adhesive test continuous
Tape adhesive surface of part of the test after Cutting Plating can not have shedding
7. 2mm line above tape adhesive test back to
eight. tail fixed In the Torque Gage,
9. the tail
10.High = 162cm 19 times down the floor (iron)
11. the middle of the push / full gauge
12 for each sample to test 10 products
已赞过 已踩过<
你对这个回答的评价是?
评论 收起
jiang615243
2012-08-09
知道答主
回答量:25
采纳率:0%
帮助的人:6.4万
展开全部
1. After the test, in room temperature (25 ℃ ± 5 ℃) on 1 hour after testing.
To meet the directory 3 (Page 6) electronics
2. To meet the directory 3 (6 Page) electronic characteristics.
No appearance damage and denaturation bad
3. Cycle: 30 cycles (each 1 hours total 60 hours (low temperature 30 hr. High temperature 30 hr.))
4. Height 152 cm. Falling nineteen times (iron plate)
5. After the experiment with distilled water after washing in 2 hours undertake in the inspection
Surface corrosion, from.
6. Tape paste test continuously 2 times
Tape after all parts of the test Cutting Plating surface can't have fall off
7. 2 mm 5 line tape above all test 2 back
8. The tail in the fixed Torque Gage.
9. The tail fixed
10. High = 162 cm 19 times fall, the floor (iron plate)
11. Among the push/full gauge
12. Each sample, test 10 products
已赞过 已踩过<
你对这个回答的评价是?
评论 收起
pivoinetmoi
2012-07-24 · TA获得超过2015个赞
知道小有建树答主
回答量:1412
采纳率:33%
帮助的人:985万
展开全部
1 after the test, it should be retest one hour after being setted in the constant temperature (25°c+5°c); the requirements that listed in the catalogue3 (6 pages) must be satisfied.

2 the specific characters which are listed in the catalogue 3(6 papes) must be confirmed. There should not be any damage in outlook and modification in nature.
3 Cycle: 30 cycles( each hour, in total 60 hours, low temperature:30hr, high temperature: 30hr)
4 samplings should be tested through the falling movements summed to 19 times from the height of 152cm
5 after the test, clean the samplings with steam water, and observe their outlook during 2 hours; The surface should not have any corrosion and brokenness
6 to conduct taping tests for twice, after which to cut down partial of sampling, the plating side should not be broken
7 2mm, above 5 ranges, taping test for twice
8 to fix the tail part on the Torque Gage
9To fix the tail part
10 height =162cm, falling tests for 19 times , the condition of the floor : iron
11 push/pull the middle part of gauge
12 to test each of the 10 samplings
本回答被网友采纳
已赞过 已踩过<
你对这个回答的评价是?
评论 收起
天下会1
2012-08-06 · TA获得超过118个赞
知道答主
回答量:392
采纳率:0%
帮助的人:135万
展开全部
1. After the test, in room temperature (25 ℃ ± 5 ℃) on 1 hour after testing.
To meet the directory 3 (Page 6) electronics
2. To meet the directory 3 (6 Page) electronic characteristics.
No appearance damage and denaturation bad
3. Cycle: 30 cycles (each 1 hours total 60 hours (low temperature 30 hr. High temperature 30 hr.))
4. Height 152 cm. Falling nineteen times (iron plate)
5. After the experiment with distilled water after washing in 2 hours undertake in the inspection
Surface corrosion, from.
6. Tape paste test continuously 2 times
Tape after all parts of the test Cutting Plating surface can't have fall off
7. 2 mm 5 line tape above all test 2 back
8. The tail in the fixed Torque Gage.
9. The tail fixed
10. High = 162 cm 19 times fall, the floor (iron plate)
11. Among the push/full gauge
12. Each sample, test 10 products
已赞过 已踩过<
你对这个回答的评价是?
评论 收起
推荐律师服务: 若未解决您的问题,请您详细描述您的问题,通过百度律临进行免费专业咨询

为你推荐:

下载百度知道APP,抢鲜体验
使用百度知道APP,立即抢鲜体验。你的手机镜头里或许有别人想知道的答案。
扫描二维码下载
×

类别

我们会通过消息、邮箱等方式尽快将举报结果通知您。

说明

0/200

提交
取消

辅 助

模 式