Question

18crnimo7-6是什么材料？热处理数据？

Answer 1

18crnimo7-6对应标准    EN 10084-1998 渗碳钢－交货技术条件 Case hardening steels. Technical delivery conditions   

用途：

广泛应用于变速箱齿轮，具有高抗弯强度、接触疲劳强度，18CrNiMo7-6还具有高的硬度和耐磨性，心部具有高的硬度和韧性。综合机械性能较高。

Answer 2

18CrNiMo7-6合金钢

18CrNiMo7-6材料号：

1.6587

18CrNiMo7-6标准：

EN 10084 : 2008     

18CrNiMo7-6特性及应用：

18CrNiMo7-6材料，德国牌号特种钢。具有高抗弯强度、接触疲劳强度，还具有高的硬度和耐磨性，心部具有高的硬度和韧性，综合机械性能较高。广泛应用于变速箱齿轮等。

18CrNiMo7-6化学成分：

碳 C：0.15 - 0.21

硅 Si：≤0.4

锰 Mn：0.5 - 0.9

镍 Ni：1.4 - 1.7

磷 P：≤ 0.025

硫 S：≤ 0.035

铬 Cr：1.5 - 1.8

钼 Mo：0.25 - 0.35

18CrNiMo7-6热处理及力学性能:

       

18CrNiMo7-6主要规格：

18CrNiMo7-6圆棒、18CrNiMo7-6锻棒、18CrNiMo7-6板、18CrNiMo7-6扁钢、18CrNiMo7-6锻件、18CrNiMo7-6锻环、18CrNiMo7-6加工件、18CrNiMo7-6管、18CrNiMo7-6锻饼

Answer 3

18crnimo7-6是合金结构钢

　　17CrNiMo6 是德国 DIN 17210-（86）标准的钢号，欧标为18CrNiMo7-6,对应GB的 17Cr2Ni2Mo 　　17Cr2Ni2Mo不是GB材料，而是JB材料。具体的标准号为：JB∕T 6395-2010大型齿轮、齿圈锻件 　　17CrNiMo6和20CrMnTi区别： 　　17CrNiMo6的韧性好得多 　　碳含量不同，合金元素不同，机械性能不同。热工艺性也不同。 　　前面的性能要优越一些，后一种变速箱齿轮、差速器齿轮普遍使用。

17CrNiMo6化学成分（质量百分比，%）：

　　碳(C)：0.15-0.20   硅(Si)：≤0.40, 　　锰(Mn)：0.40-0.60, 　　硫(S)：≤0.035, 　　磷(P)：≤0.035， 　　,铬(Cr)：1.50-1.80， 　　镍(Ni)：1.40-1.70, 　　钼(Mo)：0.25-0.35，

Answer 4

主要化学成分碳Carbon
0.18%
硅Silicon
0.20%
锰Manganese
0.70%
铬Chromium
1.65%
镍Nickel
1.55%
钼Molybdenum0.30%热处理数据HEAT TREATMENT:
Forging:
Heat to 1150°C Hold till uniform
Minimum forging temperature 850°C
Cool in ashes, warm dry lime or sand
Annealing:
Heat to 830°C – 850°C
Cool in furnace
Normalising:
Heat to 860°C – 890°C
Cool in still air
Stress Relieving:
Heat to 630°C – 650°C
Cool in still air
Carburising:
Pack, Salt or Gas carburise at 900°C – 950°C.
Core Refining:
Heat to 830°C – 870°C
Cool in air or quench in oil or into a salt bath held at 150°C – 200°C and then air cool
Case Hardening:
Heat to 780°C – 820°C
Quench in oil
Single Refine:
Suitable for fine grained steels only
Direct Quench:
Cool from carburising temperature to 820°C – 830°C and cool in air or quench in oil or into salt bath.
Alternatively cool from carburising temperature to room temperature.
Re-heat to 820°C – 830°C and cool in air or quench in oil or into salt bath.
Tempering:
Tempering at 150°C – 200°C will improve the toughness of the case with minimal effect on its hardness and reduce the possibility of grinding cracks.
Heat treatment details for guidance only如果不懂的话用google翻译一下吧，我懒得翻译了

Answer 5

热处理数据：锻造：加热到1150°C，保持直到组织均匀最低锻造温度850°C退火：加热温度：830°C-850°C ，炉冷正火： …………：860°C-890°C，空冷去应力退火：……：630°C-650°C，空冷渗碳：……：900°C-950°C心部细化：……：830°C-870°C ，空冷，油淬或者淬入150°C-200°C盐浴炉中后空冷表面强化：……：780°C-820°C，油淬淬火：
从渗碳温度冷到 820°C – 830°C 空冷或者油淬或者淬入盐浴炉中
或者选择冷到室温后再次加热到820°C – 830°C后空冷或油淬或者淬入盐浴炉中回火：在150°C – 200°C 温度回火可以提高塑韧性较小的降低硬度，减低产生磨削裂纹的可能以上热处理数据仅供参考。